Rubber Adhesion Peel Test

The value of interest is the adhesion strength defined as the maximum force divided by the.

Rubber adhesion peel test. Method b describes a peel procedure to determine the adhesive strength between rubber materials to a metal plate or substrate. Adhesion testing is a critical aspect of multi component rubber products and frequently should be considered for both rubber to rubber interfaces and rubber to reinforcement interfaces. It is related to the bonding strength of an adhesive to a mating substrate. Application spotlight peel adhesion test equipment for adhesives tapes and labels.

Adhesion testing for rubber adhesion to flexible and rigid substrates as well as the adhesive bonding of parts are an important properties for designers to understand when evaluating materials. From peel or stripping strength to measurements at temperature ardl can provide the. This test standard is divided into methods a through h. Ardl offers a variety of tests to evaluate the adhesion properties of materials and components.

Common application examples that use tests in astm d429 are vehicle engine mounts vehicle suspension bushings rubber coated metal parts and rubber lined tanks and containers. Method a describes a tension test used to determine the bond of a rubber part assembled between two parallel metal plates. 1 1 this test method covers the determination of peel adhesion of reinforcing fabrics that are bonded to rubber compounds. Adhesive properties for pressure sensitive labels packages and tapes are measured using a standard test surface a specified angle and test speed.

The rubber proofed fabric was subjected to ozone irradiation at different doses 250 500 and 1000 ppb. Tack is defined as the force required to separate two sheet materials which are compressed together for a specified. Picma tack tester the picma tack tester measures the adhesion or tack of rubber materials adhesive tapes sealants and other materials. The last comes first.

The peel strength was used to measure the adhesion strength between the fabric and the rubber. Some of the very first applications for pressure sensitive adhesives such as bandages labels and masking tapes for painting were evaluated on performance based on how easy or how difficult it was to remove them from the applied surfaces. It is applicable to either woven or parallel cord textile structures from both natural and manmade fibers and to parallel steel cord structures.